| SKU | KY-CM211106 |
| Core dimensions（OD×ID×HT） | Φ21×11×06 mm |
| Finished core dimensions: | 30*16 mm |
| Effictive cross section: | 0.3 cm2 |
| Mean path length: | 5.02 cm |
| Coiling | 1.0 Coiling 32.5Ts |
| AL Nominal Value(10kHz) | —— |
| AL Nominal Value(100kHz) | —— |
| Amorphous 1K107 | |||
| Saturate induction / Bs (T) | 1.25 | Magnetostriction / λs | 1x10⁻⁶ |
| Curie temperature (℃) | 570 | Density ρ (g/cm³) | 7.2 |
| Crystallization (℃) | 530 | Resistivity δ (μΩ.cm） | 120 |
| Hardness / Hv | 960 | Thickness (μm) | 28~35 |
high frequency, small size
2<50w/kg@100kHz，300mT
Hc<1.5A/m
low working noise
Excellent broadband characteristic and highimpedance
Adjustable magnetic property can satisfy the request of low remanence, high rectangular ratio and high initial permeability
Permeability/Frequency relative change curve
B H curve of different magnetic materials
Hysteresis loop lof different magnetic materials
Permeability/Temperature relative change curve
| ltem | Nano crystalline iron core | Ferrite core |
| Magnetic saturation induction intensity Bs(T) | ≥1.2 | 0.4 |
| Curie temperature Tc(℃) | ≥570 | 170 |
| Saturation magnetostriction coefficient( λ s) | 2x10-6 | 4x10-6 |
| Working temperature(℃) | -55℃-130℃ | <80℃ |
| Initial permeability( μ o) | 20000-160000 | 2000 |
| Goercivity He(A/m) | <1.6 | 30 |
| High frequency lossP(20kHz.0.2T) | 3.4 | 7.5 |
| Kayo Part No. | Core dimensions | Finished core dimensions | Effictive cross section | Mean path length | Coiling | AL Nominal Value** | Specification Table | |
| OD×ID×HT | OD×HT | AFe | lFe | 10kHz | 100kHz | |||
| mm | mm | cm2 | cm | μH | μH | |||
| KY-CM504020 | Φ50×40×20 | 65*36 | 1.0 | 14.13 | 2.0 Coiling*3P 6Ts | 33 MIN | 11 MIN | |
| KY-CM504020 | Φ50×40×20 | 65*36 | 1.0 | 14.13 | 2.2 Coiling*3P 6Ts | 33 MIN | 11 MIN | |
| KY-CM504020 | Φ50×40×20 | 65*36 | 1.0 | 14.13 | 2.4 Coiling*3P 6Ts | 33 MIN | 11 MIN | |
| KY-CM322010 | Φ32×20×10 | 44*23 | 0.6 | 8.16 | 1.8 Coiling*2P 13Ts | - | 11 MIN | |
| KY-CM181110 | Φ18×11×10 | 26*21 | 0.35 | 4.55 | 0.8 Coiling 29Ts | - | - | |
| KY-CM211106 | Φ21×11×06 | 30*16 | 0.3 | 5.02 | 1.0 Coiling 32.5Ts | - | - | |
| KY-CM181245 | Φ18×12×4.5 | 25*15 | 0.14 | 4.71 | 1.3 Coiling*2P 32.5Ts | 1.0 | - | |
Note: Other dimmension and performance can be customized
Used In Current Transformer
Used In Current Transformer
Used In Current Transformer
Used In Current Transformer
We are based in Henan, China, start from 2011,sell to Eastern Europe(30.00%),South America(20.00%),South Asia(20.00%),North America(15.00%),Southeast Asia(15.00%).
Always a pre-production sample before mass production;
Always final Inspection before shipment;
Nanocrystalline common-mode inductor core,Core for DC resistant current transformers,Current transformer core,Cobalt-based amorphous alloy strip,Iron-based amorphous filter inductor core.
"To provide reliable quality, competitive products in price, and common development with customers" is our enterprise vision.AnYang Kayo is one of the leaders in the amorphous industry in northern China. In the past ten years, Kayo has been working hard.